特 性
Properties
|
試驗方法
Test
Methods
|
實驗狀況
Test Conditions
|
單 位
Units
|
D-350
|
D-350N
|
D-380
|
衝擊強度
Izod Impact Strength
Notched |
1/4" bar
|
ASTM
D-256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
27
265
4.96
|
27
265
4.96
|
18
176
3.3
|
|
1/8" bar
|
ASTM
D-256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
30
294
5.51
|
30
294
5.51
|
20
196
3.7
|
抗張強度
Tensile Strength At
Yield Type 1, 1/8" Thickness |
ASTM
D-638
50 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
400
39.2
5.68
|
400
39.2
5.68
|
470
46.1
6.68
|
抗折強度
Flexural Strength
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
650
63.7
9.23
|
650
63.7
9.23
|
650
73.5
10.7
|
抗折模數
Flexural Modulus
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
GPa
psix105
|
21000
2.06
2.98
|
21000
2.06
2.98
|
24000
2.35
3.41
|
洛式硬度
Rockwell Hardness |
ASTM
D-785
|
23℃
(73℉)
|
R Scale
|
101
|
101
|
111
|
熱變形溫度(Unannealed)
Heat Deflection Temperature
1/2"×1/2"×5" bar |
ASTM
D-648 |
18.6 Kgf/cm2
(264 psi) |
℃
℉ |
87
189
|
87
189
|
88
190
|
熱軟化點溫度
Vicat Softening Temperature |
ASTM
D-1525
|
Load
1 Kg
|
℃
℉
|
104
219
|
104
219
|
104
219
|
融流指數
Melting Flow Rate |
ASTM
D-1238
|
200℃
5 Kg
|
g/10min.
|
5
|
3.5
|
5
|
比重
Specific Gravity |
ASTM
D-792
|
23℃
(73℉)
|
|
1.03
|
1.03
|
1.04
|
UL燃燒等級
UL Flame Class Rating
(File No. E88637)
(C-UL CSA LS 103112) |
UL 94
|
|
1/8"
Thickness
|
HB
|
---
|
HB
|
|
1/16"
Thickness
|
HB
|
---
|
HB
|
成型收縮率
Mold Shrinkage Rate |
ASTM
D-955
|
|
%
|
0.3-0.6
|
|
|