特 性
Properties
|
試驗方法
Test
Methods
|
實驗狀況
Test
Conditions
|
單 位
Units
|
D-180
|
D-150
|
D-150A
|
衝擊強度
Izod Impact Strength
Notched |
1/4" bar
|
ASTM
D-256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
16
157
2.90
|
22
216
4.04
|
22
216
4.04
|
|
1/8" bar
|
ASTM
D-256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
18
176
3.3
|
24
235
4.41
|
24
216
4.04
|
抗張強度
Tensile Strength At
Yield Type 1, 1/8" Thickness |
ASTM
D-638
50 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
510
50
7.24
|
500
49
7.11
|
500
49
7.11
|
抗折強度
Flexural Strength
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
820
80.4
11.64
|
800
78.5
11.36
|
800
82.3
11.36
|
抗折模數
Flexural Modulus
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
GPa
psix105
|
26000
2.55
3.69
|
25000
2.45
3.55
|
25000
2.45
3.55
|
洛式硬度
Rockwell Hardness |
ASTM
D-785
|
23℃
(73℉)
|
R Scale
|
113
|
112
|
112
|
熱變形溫度(Unannealed)
Heat Deflection Temperature
1/2"×1/2"×5" bar |
ASTM
D-648 |
18.6 Kgf/cm2
(264 psi) |
℃
℉ |
90
194
|
89
192
|
89
192
|
熱軟化點溫度
Vicat Softening Temperature |
ASTM
D-1525
|
Load
1 Kg
|
℃
℉
|
106
223
|
105
221
|
105
221
|
融流指數
Melting Flow Rate |
ASTM
D-1238
|
200℃
5 Kg
|
g/10min.
|
2.5
|
2.3
|
2.3
|
比重
Specific Gravity |
ASTM
D-792
|
23℃
(73℉)
|
---
|
1.05
|
1.05
|
1.05
|
UL燃燒等級
UL Flame Class Rating
(File No. E88637)
(C-UL CSA LS 103112) |
UL 94
|
|
1/8"
Thickness
|
HB
|
HB
|
HB
|
|
1/16"
Thickness
|
HB
|
HB
|
HB
|
成型收縮率
Mold Shrinkage Rate |
ASTM
D-955
|
|
%
|
0.3-0.6
|
0.3-0.6
|
0.3-0.6
|