特 性
Properties
|
试验方法
Test
Methods
|
实验状况
Test
Conditions
|
单 位
Units
|
D-100
|
D-120
|
D-120S
|
冲击强度
Izod Impact Strength
Notched |
1/4" bar
|
ASTM
D256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
45
441
8.26
|
36
353
6.61
|
40
392
7.34
|
|
1/8" bar
|
ASTM
D256
Method A
|
23℃
(73℉)
|
Kgf-cm/cm
J/M
ft-1bs/in.
|
53
519
9.73
|
45
441
8.26
|
52
510
9.54
|
抗张强度
Tensile Strength At Yield
Type 1, 1/8" Thickness |
ASTM
D638
50 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
380
37.2
5.4
|
440
43.1
6.25
|
480
47
6.82
|
抗折强度
Flexural Strength
1/8"×1"×4" bar |
ASTM
D790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
MPa
psix103
|
610
59.8
8.66
|
710
69.6
10.08
|
740
72.6
10.50
|
抗折系数
Flexural Modulus
1/8"×1"×4" bar |
ASTM
D790
15 mm/min
|
23℃
(73℉)
|
Kgf/cm2
GPa
psix105
|
19000
1.86
2.7
|
22000
2.16
3.12
|
23000
2.25
3.27
|
洛式硬度
Rockwell Hardness |
ASTM
D785
|
23℃
(73℉)
|
R Scale
|
93
|
102
|
104
|
热变形温度(Unannealed)
Heat Deflection Temperature
1/2"×1/2"×5" bar |
ASTM
D-648 |
18.6 Kgf/cm2
(264 psi) |
℃
℉ |
87
189
|
87
189
|
88
190
|
热软化点温度
Vicat Softening Temperature |
ASTM
D1525
|
Load
1 Kg
|
℃
℉
|
104
219
|
104
219
|
104
219
|
融流指数
Melting Flow Rate |
ASTM
D1238
|
200℃
5 Kg
|
g/10min.
|
0.5
|
1.1
|
0.8
|
比重
Specific Gravity |
ASTM
D792
|
23℃
(73℉)
|
--
|
1.03
|
1.03
|
1.04
|
UL燃烧等级
UL Flame Class Rating
(File No. E88637)
(C-UL CSA LS 103112) |
UL 94
|
|
1/8"
Thickness
|
HB
|
HB
|
(HB)
|
|
1/16"
Thickness
|
HB
|
HB
|
(HB)
|
成型收缩率
Mold Shrinkage Rate |
ASTM
D955
|
|
%
|
0.3-0.6
|
0.3-0.6
|
0.3-0.6
|